展羽塑胶 >> 塑胶物性 >> Delrin® 100P NC010英文物性表

Delrin® 100P NC010英文物性表

Delrin® 100P NC010

ACETAL RESIN

DuPont Performance Polymers

Product Description:

High Viscosity Acetal Homopolymer with Improved Processing

Units: SI | English

General

Material Status

Commercial: Active

Literature 1

Processing - Injection Molding (English)

Typical Processing for DuPont Engineering Polymers (English)

White Paper - Property Advantages of Delrin® Acetal Homopolymer - a guide for design engineers (English)

UL Yellow Card 2

E41938-257616

Search for UL Yellow Card

DuPont Performance Polymers

Delrin®

Availability

Africa & Middle East

Asia Pacific

Europe

Latin America

North America

Additive

Lubricant

Mold Release

Features

Good Processability

High Viscosity

Homopolymer

RoHS Compliance

Contact Manufacturer

Forms

Pellets

Processing Method

Extrusion

Injection Molding

Profile Extrusion

Sheet Extrusion

Multi-Point Data

Isothermal Stress vs. Strain (ISO 11403-1)

Secant Modulus vs. Strain (ISO 11403-1)

Shear Modulus vs. Temperature (ISO 11403-1)

Shear Modulus vs. Temperature, Dynamic (ISO 11403-1)

Shear Stress vs. Shear Rate (ISO 11403-1)

Specific Volume vs Temperature (ISO 11403-2)

Tensile Modulus vs. Temperature (ISO 11403-1)

Viscosity vs. Shear Rate (ISO 11403-2)

Part Marking Code (ISO 11469)

>POM<

Resin ID (ISO 1043)

Physical	Nominal Value	Unit	Test Method
Density	1.42	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR)	2.6	g/10 min	ISO 1133
Melt Volume-Flow Rate (MVR) (190°C/2.16 kg)	0.134	in³/10min	ISO 1133
Molding Shrinkage			ISO 294-4
Across Flow	1.9	%
Flow	2.2	%
Water Absorption			ISO 62
Saturation, 73°F, 0.0787 in	1.4	%
Equilibrium, 73°F, 0.0787 in, 50% RH	0.30	%
Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness			ISO 2039-2
M-Scale	88
R-Scale	119

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	428000	psi	ISO 527-2
Tensile Stress (Yield)	10300	psi	ISO 527-2
Tensile Strain (Yield)	25	%	ISO 527-2
Nominal Tensile Strain at Break	45	%	ISO 527-2
Tensile Creep Modulus			ISO 899-1
1 hr	392000	psi
1000 hr	218000	psi
Flexural Modulus	413000	psi	ISO 178
Flexural Stress (3.5% Strain)	11200	psi	ISO 178
Poisson's Ratio	0.35		ISO 527
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-22°F	6.7	ft·lb/in²
73°F	7.1	ft·lb/in²
Charpy Unnotched Impact Strength			ISO 179/1eU
-22°F	190	ft·lb/in²
73°F	No Break
Notched Izod Impact Strength			ISO 180/1A
-40°F	5.7	ft·lb/in²
73°F	6.7	ft·lb/in²

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
66 psi, Unannealed	311	°F	ISO 75-2/B
264 psi, Unannealed	203	°F	ISO 75-2/A
Vicat Softening Temperature
--	347	°F	ISO 306/A50
--	320	°F	ISO 306/B50
Melting Temperature 3	352	°F	ISO 11357-3
CLTE			ISO 11359-2
Flow	6.1E-5	in/in/°F
Flow : -40 to 73°F	5.6E-5	in/in/°F
Transverse	6.1E-5	in/in/°F
Transverse : -40 to 73°F	5.6E-5	in/in/°F
Annealing Temperature	320	°F
Annealing Time - Optional	30.0	min/mm

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	2.0E+13	ohms	IEC 60093
Volume Resistivity	1.0E+14	ohms·cm	IEC 60093
Electric Strength	1000	V/mil	IEC 60243-1
Relative Permittivity			IEC 60250
100 Hz	3.90
1 MHz	3.90
Dissipation Factor			IEC 60250
100 Hz	3.5E-3
1 MHz	5.5E-3
Comparative Tracking Index	600	V	IEC 60112
Flammability	Nominal Value	Unit	Test Method
Burning Rate 4 (0.0394 in)	2.0	in/min	ISO 3795
Flame Rating
0.031 in	HB		UL 94
0.06 in	HB		UL 94, IEC 60695-11-10, -20
0.03 in	HB		IEC 60695-11-10, -20
FMVSS Flammability	B		FMVSS 302

Fill Analysis	Nominal Value	Unit	Test Method
Melt Density	1.19	g/cm³
Specific Heat Capacity of Melt	0.717	Btu/lb/°F
Thermal Conductivity of Melt	1.5	Btu·in/hr/ft²/°F
Additional Information	Nominal Value	Unit	Test Method
Emission	< 8.00	mg/kg	VDA 275

Injection	Nominal Value	Unit
Drying Temperature	176	°F
Drying Time - Desiccant Dryer	2.0 to 4.0	hr
Suggested Max Moisture	0.20	%
Processing (Melt) Temp	410 to 428	°F
Melt Temperature, Optimum	419	°F
Mold Temperature	176 to 212	°F
Mold Temperature, Optimum	194	°F
Holding Pressure	13100 to 16000	psi
Drying Recommended	yes
Hold Pressure Time	8.00	s/mm
Extrusion	Nominal Value	Unit
Drying Temperature	167 to 185	°F
Drying Time	2.0 to 4.0	hr
Suggested Max Moisture	0.20	%
Melt Temperature	383 to 401	°F
Extrusion Melt Temperature, Optimum	392	°F