展羽塑胶 >> 塑胶物性 >> Delrin® 100ST NC010 英文物性表

Delrin® 100ST NC010 英文物性表

Delrin® 100ST NC010

ACETAL RESIN

DuPont Performance Polymers

Product Description:

Super Toughened High Viscosity Acetal Homopolymer

Units: SI | English

General

Material Status

Commercial: Active

Literature 1

Processing - Injection Molding (English)

Typical Processing for DuPont Engineering Polymers (English)

White Paper - Property Advantages of Delrin® Acetal Homopolymer - a guide for design engineers (English)

UL Yellow Card 2

E41938-257617

Search for UL Yellow Card

DuPont Performance Polymers

Delrin®

Availability

Africa & Middle East

Asia Pacific

Europe

Latin America

North America

Additive

Lubricant

Mold Release

Features

High Viscosity

Homopolymer

RoHS Compliance

Contact Manufacturer

Forms

Pellets

Processing Method

Extrusion

Injection Molding

Profile Extrusion

Sheet Extrusion

Multi-Point Data

Creep Modulus vs. Time (ISO 11403-1)

Isochronous Stress vs. Strain (ISO 11403-1)

Isothermal Stress vs. Strain (ISO 11403-1)

Secant Modulus vs. Strain (ISO 11403-1)

Shear Modulus vs. Temperature (ISO 11403-1)

Shear Modulus vs. Temperature, Dynamic (ISO 11403-1)

Shear Stress vs. Shear Rate (ISO 11403-1)

Specific Volume vs Temperature (ISO 11403-2)

Tensile Modulus vs. Temperature, Dynamic (ISO 11403-1)

Viscosity vs. Shear Rate (ISO 11403-2)

Part Marking Code (ISO 11469)

>POM-HI<

Resin ID (ISO 1043)

POM-HI

Physical	Nominal Value	Unit	Test Method
Density	1.34	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR)	2.0	g/10 min	ISO 1133
Melt Volume-Flow Rate (MVR) (190°C/2.16 kg)	0.104	in³/10min	ISO 1133
Molding Shrinkage			ISO 294-4
Across Flow	1.4	%
Flow	1.3	%
Water Absorption			ISO 62
Saturation, 73°F, 0.0787 in	0.90	%
Equilibrium, 73°F, 0.0787 in, 50% RH	0.35	%
Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness			ISO 2039-2
M-Scale	58
R-Scale	105

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	203000	psi	ISO 527-2
Tensile Stress (Yield)	5950	psi	ISO 527-2
Tensile Strain (Yield)	30	%	ISO 527-2
Nominal Tensile Strain at Break	> 50	%	ISO 527-2
Tensile Creep Modulus			ISO 899-1
1 hr	160000	psi
1000 hr	79800	psi
Flexural Modulus	160000	psi	ISO 178
Flexural Stress (3.5% Strain)	4930	psi	ISO 178
Coefficient of Friction (vs. Itself - Dynamic, 1 hr)	0.32		ASTM D1894
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-22°F	8.6	ft·lb/in²
73°F	43	ft·lb/in²
Charpy Unnotched Impact Strength			ISO 179/1eU
-22°F	No Break
73°F	No Break
Notched Izod Impact Strength			ISO 180/1A
-40°F	9.5	ft·lb/in²
73°F	43	ft·lb/in²

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
66 psi, Unannealed	212	°F	ISO 75-2/B
264 psi, Unannealed	140	°F	ISO 75-2/A
Glass Transition Temperature 3	-31.0	°F	ISO 11357-2
Melting Temperature 3	352	°F	ISO 11357-3
CLTE			ISO 11359-2
Flow	7.2E-5	in/in/°F
Transverse	7.8E-5	in/in/°F
Annealing Temperature	320	°F
Annealing Time - Optional	30.0	min/mm
Effective Thermal Diffusivity	6.00E-8	m²/s

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+14	ohms	IEC 60093
Volume Resistivity	1.0E+14	ohms·cm	IEC 60093
Relative Permittivity			IEC 60250
100 Hz	4.40
1 MHz	3.80
Comparative Tracking Index	600	V	IEC 60112
Flammability	Nominal Value	Unit	Test Method
Burning Rate 4 (0.0394 in)	1.6	in/min	ISO 3795
Flame Rating (0.06 in)	HB		UL 94, IEC 60695-11-10, -20
FMVSS Flammability	B		FMVSS 302

Fill Analysis	Nominal Value	Unit	Test Method
Melt Density	1.14	g/cm³
Additional Information	Nominal Value	Unit	Test Method
Emission	< 8.00	mg/kg	VDA 275
Specific Wear - Against itself	2980	10^-10 in³·min/ft·lb·hr	ASTM D1894

Injection	Nominal Value	Unit
Drying Temperature	176	°F
Drying Time - Desiccant Dryer	2.0 to 4.0	hr
Suggested Max Moisture	0.050	%
Processing (Melt) Temp	392 to 410	°F
Melt Temperature, Optimum	401	°F
Mold Temperature	104 to 140	°F
Mold Temperature, Optimum	122	°F
Holding Pressure	8700 to 11600	psi
Drying Recommended	yes
Hold Pressure Time	7.50	s/mm
Extrusion	Nominal Value	Unit
Drying Temperature	167 to 185	°F
Drying Time	2.0 to 4.0	hr
Suggested Max Moisture	0.050	%
Melt Temperature	383 to 401	°F
Extrusion Melt Temperature, Optimum	392	°F